dc.description.abstractEn este trabajo se presenta un análisis de los resultados del crecimiento y caracterización de capas Co, CoCu y CoCuCo y de las láminas de Cu que se usaron como sustrato. El crecimiento de las capas se realizó utilizando la técnica de electrodeposición química. Se estableció la calidad cristalina de las láminas de Cu y de los diferentes crecimientos de Co y Cu mediante DRX, estableciéndose que las láminas de Cu con tratamiento térmico y químico presentaban mejor calidad. Las diferentes láminas de Cu se analizaron mediante difracción de rayos X (DRX) para determinar su calidad cristalina; para establecer la morfología y composición elemental de cada una de las láminas se usó microscopía electrónica de barrido (MEB) y espectrometría de dispersión de energía (EDE), esto se hizo con el fin de definir que sustrato era más apropiado para los crecimientos. Teniendo en cuenta los resultados obtenidos, se realizó tratamiento químico y tratamiento térmico y químico, para definir cuál de estos dos tratamientos permitía mejorar la calidad de la superficie con respecto a las condiciones iniciales. Luego de establecer el sustrato más adecuado, se realizaron crecimientos de Co variando el tiempo de deposición y la concentración del electrolito, buscando encontrar los parámetros que permiten tener mejores resultados y así, establecerlos como parámetros fijos. Posterior a esto se realizaron los crecimientos de Co, CoCu y CoCuCo cambiando la preparación del electrolito. Estas capas se analizaron mediante difracción de rayos X (DRX), microscopia electrónica de barrido (MEB) y espectrometría de dispersión de energía (EDE). Tanto al sustrato usado para los crecimientos como al crecimiento que presentó mayor cantidad de Co, se les midió la magnetización a través del magnetómetro de muestra vibrante (MMV). Las capas de Co/Cu, CoCu/Cu y CoCuCo/Cu que presentaron mejor calidad cristalina, morfología y comportamiento magnético fueron las depositadas usando los siguientes parámetros: 1) tiempo de deposición: 1000s, 2) concentración del electrolito: [0,3]M y 3) sal usada para la preparación del electrolito: sulfato de Co. Las anteriores características están en concordancia con los resultados reportados en la literatura / Abstract: In this work are presented and discussed the growth and characterization results of Co, CoCu and CoCuCo layers and Cu foils were used as substrate. The growth of the layers was done using the chemical electrodeposition technique. The different Cu foils were analyzed by X-ray diffraction (XRD) to determine their crystalline quality, to establish the morphology and elemental composition of each layers was used scanning electron microscopy (SEM) and energy dispersion spectrometry (EDE), this was done in order to identify which was more suitable substrate for growth. Taking into account the results obtained was carried out chemical and chemical and thermal processing, to determine which of these allowed to improve the surface quality with respect to initial conditions. After establishing the most suitable substrate was made Co growth varying the deposition time and electrolyte concentration, seeking to find the parameters that allow better results and thus establish as a fixed parameters. After this is done the Co, CoCu CoCuCo growth changing the electrolyte preparation. These layers were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersion spectroscopy (EDE). Both the substrate used for growth as growth that showed higher amount of Co, the magnetization was measured by vibrating sample magnetometer (MMV). Co/Cu, CoCu/Cu and CoCuCo/Cu layers which showed better crystalline quality, morphology and magnetic behavior were deposited using the following parameters: 1) deposition time: 1000s, 2) the electrolyte concentration [0.3]M and 3) salt used for electrolyte preparation: Co sulfate. The above features are consistent with the results reported in the literature
dc.format.mimetypeapplication/pdf
dc.language.isospa
dc.relation.ispartofUniversidad Nacional de Colombia Sede Manizales Facultad de Ciencias Exactas y Naturales Departamento de Física y Química
dc.relation.ispartofDepartamento de Física y Química
dc.rightsDerechos reservados - Universidad Nacional de Colombia
dc.rights.urihttp://creativecommons.org/licenses/by-nc/4.0/
dc.subject.ddc66 Ingeniería química y Tecnologías relacionadas/ Chemical engineering
dc.subject.ddc62 Ingeniería y operaciones afines / Engineering
dc.subject.ddc54 Química y ciencias afines / Chemistry
dc.titleSíntesis y caracterización de capas de CoCuCo/Cu obtenidas por electrodeposición química
dc.typeTrabajo de grado - Maestría
dc.type.driverinfo:eu-repo/semantics/masterThesis
dc.type.versioninfo:eu-repo/semantics/acceptedVersion
dc.identifier.eprintshttp://bdigital.unal.edu.co/2105/
dc.description.degreelevelMaestría
dc.relation.referencesGiraldo Betancur, Astrid Lorena (2009) Síntesis y caracterización de capas de CoCuCo/Cu obtenidas por electrodeposición química. Maestría thesis, Universidad Nacional de Colombia - Sede Manizales.
dc.rights.accessrightsinfo:eu-repo/semantics/openAccess
dc.subject.proposalCobalto,Cobre, Galvanoplastia, Películas delgadas, microscopía electrónica de barrido (MEB), Espectrometría de dispersión de energía (EDE), Producción de multicapas metálicas
dc.type.coarhttp://purl.org/coar/resource_type/c_bdcc
dc.type.coarversionhttp://purl.org/coar/version/c_ab4af688f83e57aa
dc.type.contentText
dc.type.redcolhttp://purl.org/redcol/resource_type/TM
oaire.accessrightshttp://purl.org/coar/access_right/c_abf2


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

Atribución-NoComercial 4.0 InternacionalThis work is licensed under a Creative Commons Reconocimiento-NoComercial 4.0.This document has been deposited by the author (s) under the following certificate of deposit