Evaluating the corrosion resistance of ubm-deposited cr/crn multilayers
dc.rights.license | Atribución-NoComercial 4.0 Internacional |
dc.contributor.author | Chipatecua Godoy, Yuri Lizbeth |
dc.contributor.author | Marulanda Cardona, Diana Maritza |
dc.contributor.author | Olaya Flórez, Jhon Jairo |
dc.date.accessioned | 2019-06-27T22:57:43Z |
dc.date.available | 2019-06-27T22:57:43Z |
dc.date.issued | 2011 |
dc.identifier.uri | https://repositorio.unal.edu.co/handle/unal/33467 |
dc.description.abstract | This work was aimed at evaluating the corrosion resistance of multilayer Cr/CrN coatings deposited by the unbalan-ced magnetron sputtering (UBM) technique. Coatings were produced at room temperature using 400 mA discharge current, 9 sccm argon flow and 3 sccm nitrogen flow. The total thickness of coatings deposited on AISI 304 stainless steel and silicon (100) varied between 0.2 a 3 μm as bilayer period varied between 20 and 200 nm. Coating microstructure and chemical composition was stu-died through scanning electron microscopy (SEM) and tex-ture and crystalline phases were analysed by X-ray diffraction (XRD) before and after corrosion tests which were carried out by potentiodynamic polarisation using 0.5 M H2SO4 + 0.05M KSCN solution. Lower bilayer period coatings presented better corrosion resistance and their corrosion mechanism is discussed in this article. |
dc.description.abstract | En este artículo se evalúa la resistencia a la corrosión de los recubrimientos en multicapa de Cr/CrN depositados mediante la técnica de sputtering con magnetrón desba-lanceado, UBM. Los recubrimientos se produjeron a tem-peratura ambiente, con corriente de descarga de 400 mA y flujos de Ar de 9 sccm y de N2 de 3 sccm. El espesor total de los recubrimientos depositados sobre los sustratos de acero inoxidable AISI 304 y silicio (100) se varió entre 0,2 y 3 μm, al igual que el periodo de la bicapa, que estuvo entre 20 y 200 nm. La microestructura y compo-sición química de los recubrimientos se analizó por medio de microscopía electrónica de barrido (SEM), y la textura y fases cristalinas con difracción de rayos X (XRD), antes y después de las pruebas de corrosión, las cuales se rea-lizaron con ensayos de polarización potenciodinámica empleando una solución de 0,5M H2SO4 + 0,05M KSCN. Los recubrimientos con menor período de la bica-pa presentaron la mejor resistencia a la corrosión y su mecanismo de corrosión se discute en este estudio. |
dc.format.mimetype | application/pdf |
dc.language.iso | spa |
dc.publisher | Universidad Nacional de Colombia - Facultad de Ingeniería |
dc.relation | http://revistas.unal.edu.co/index.php/ingeinv/article/view/20515 |
dc.relation.ispartof | Universidad Nacional de Colombia Revistas electrónicas UN Ingeniería e Investigación |
dc.relation.ispartof | Ingeniería e Investigación |
dc.relation.ispartofseries | Ingeniería e Investigación; Vol. 31, núm. 1 (2011); 16-25 Ingeniería e Investigación; Vol. 31, núm. 1 (2011); 16-25 2248-8723 0120-5609 |
dc.rights | Derechos reservados - Universidad Nacional de Colombia |
dc.rights.uri | http://creativecommons.org/licenses/by-nc/4.0/ |
dc.title | Evaluating the corrosion resistance of ubm-deposited cr/crn multilayers |
dc.type | Artículo de revista |
dc.type.driver | info:eu-repo/semantics/article |
dc.type.version | info:eu-repo/semantics/publishedVersion |
dc.identifier.eprints | http://bdigital.unal.edu.co/23547/ |
dc.identifier.eprints | http://bdigital.unal.edu.co/23547/2/ |
dc.identifier.eprints | http://bdigital.unal.edu.co/23547/3/ |
dc.relation.references | Chipatecua Godoy, Yuri Lizbeth and Marulanda Cardona, Diana Maritza and Olaya Flórez, Jhon Jairo (2011) Evaluating the corrosion resistance of ubm-deposited cr/crn multilayers. Ingeniería e Investigación; Vol. 31, núm. 1 (2011); 16-25 Ingeniería e Investigación; Vol. 31, núm. 1 (2011); 16-25 2248-8723 0120-5609 . |
dc.rights.accessrights | info:eu-repo/semantics/openAccess |
dc.subject.proposal | sputtering con magnetrón desbalancea-do |
dc.subject.proposal | polarización potenciodinámica |
dc.subject.proposal | películas delgadas |
dc.subject.proposal | resistencia a la corrosión |
dc.subject.proposal | Cr/CrN. |
dc.subject.proposal | Unbalanced magnetron sputtering |
dc.subject.proposal | potentiodynamic polarisation |
dc.subject.proposal | thin film |
dc.subject.proposal | corrosion resistance |
dc.subject.proposal | Cr/CrN. |
dc.type.coar | http://purl.org/coar/resource_type/c_6501 |
dc.type.coarversion | http://purl.org/coar/version/c_970fb48d4fbd8a85 |
dc.type.content | Text |
dc.type.redcol | http://purl.org/redcol/resource_type/ART |
oaire.accessrights | http://purl.org/coar/access_right/c_abf2 |
Archivos en el documento
Este documento aparece en la(s) siguiente(s) colección(ones)
-
Ingeniería e Investigación [1332]
![Atribución-NoComercial 4.0 Internacional](/themes/Mirage2//images/creativecommons/cc-generic.png)