Corrosion inhibition of biodegradable chemical compounds (L-leucine and trypsin complex) on high carbon steel in 1 M H2SO4 acid media was evaluated with potentiodynamic polarization technique, weight loss analysis, open circuit potential measurement, optical microscopy, and ATR-FTIR spectroscopy. Data obtained showed the mixture has a maximum inhibition efficiency of 82.4% and 90.08% from the electrochemical tests with mixed type inhibition properties. The addition of the mixture shifts significantly the corrosion potential of the steel to passivation values from open circuit potential measurement. Results from thermodynamic calculations indicated chemisorption adsorption mechanism according to Langmuir, Freundlich, and Frumkin isotherms coupled with correlation coefficients of 0.9994, 0.9651 and 0.8834. Statistical analysis showed exposure time to be the most significant variable responsible for corrosion inhibition. Identified functional groups of the compound from ATF-FTIR spectroscopy were adsorbed completely on the carbon steel surface from observation of the decreased peak intensity. Optical microscopy images of the inhibited and uninhibited steel surfaces contrast each other with due to the presence of macro-pits and porous oxide on the uninhibited steel.Se evaluó la inhibición de la corrosión por parte de compuestos químicos biodegradables (complejo de L-leucina y tripsina) sobre acero de alto contenido de carbono en H2SO4 1 M a través de técnica de polarización potenciodinámica, análisis de pérdida de peso, medición de potencial de circuito abierto, microscopía óptica y espectroscopia ATR-FTIR. Los datos obtenidos mostraron que la mezcla tiene una eficacia de inhibición máxima de 82,4% y 90,08%, a partir de las pruebas electroquímicas con propiedades de inhibición de tipo mixto. La adición de la mezcla cambia significativamente el potencial de corrosión del acero a los valores de pasivación de la medición del potencial de circuito abierto. Los resultados de los cálculos termodinámicos indicaron un mecanismo de adsorción por quimisorción de acuerdo con las isotermas Langmuir, Freundlich y Frumkin, acopladas con coeficientes de correlación de 0,9994; 0,9651 y 0,8834, respectivamente. El análisis estadístico mostró que el tiempo de exposición es la variable más importante en la inhibición de la corrosión. Los grupos funcionales de la mezcla, identificados mediante espectroscopía ATF-FTIR, fueron completamente adsorbidos en la superficie de acero al carbono; esto se dedujo a partir de la observación de la disminución de la intensidad de pico. Las imágenes de microscopía óptica de las superficies de acero inhibidas y desinhibidas contrastan entre sí, debido a la presencia de macro-pozos y óxido poroso en el acero desinhibido.Foram feitos estudos de inibição da corrosão de compostos químicos biodegradáveis ccomplexo de L-leucina e tripsina) em aço de alto conteúdo de carbono em meio de H2SO4 1 M, estes foram avaliados com técnica de polarização potenciodinâmica, análise de perda de peso, medição de potencial de circuito aberto, microscopia óptica e espectroscopia ATR-FTIR. Os dados obtidos mostram que a mistura tem uma eficiência de inibição máxima de 82,4% e 90,08% dos testes eletroquímicos com propriedades de inibição do tipo misto. A adição da mistura desloca significativamente o potencial de corrosão do aço para valores de passivação da medição de potencial de circuito aberto. Os resultados dos cálculos termodinâmicos indicam o mecanismo de adsorção de quimisorção de acordo com as isotermas de Langmuir, Freundlich e Frumkin, juntamente com coeficientes de correlação de 0,9994; 0,9651 e 0,8834 respectivamente. A análise estatística mostrou que o tempo de exposição é a variável mais significativa da inibição da corrosão. Os grupos funcionais identificados pela espectroscopia ATF-FTIR foram completamente adsorvidos na superfície do aço ao carbono, de acordo com a observação da intensidade de pico diminuída. As imagens de microscopia óptica das superfícies de aço inibidas e desinibidas contrastam entre si devido à presença de macro-poços e óxido poroso no aço desinibido.